Structure, Atomistic Simulations, and Phase Transition of Stoichiometric Yeelimite

Abstract

ABSTRACT: Yeelimite, Ca4[Al6O12]SO4, is outstanding as an aluminate sodalite, being the framework of these type of materials flexible and dependent on ion sizes and anion ordering/disordering. On the other hand, yeelimite is also important from an applied perspective as it is the most important phase in calcium sulfoaluminate cements. However, its crystal structure is not well studied. Here, we characterize the room temperature crystal structure of stoichiometric yeelimite through joint Rietveld refinement using neutron and Xray powder diffraction data coupled with chemical soft-constraints. Our structural study shows that yeelimite has a lower symmetry than that of the previously reported tetragonal system, which we establish to likely be the acentric orthorhombic space group Pcc2, with a √2a × √2a × a superstructure based on the cubic sodalite structure. Final unit cell values were a = 13.0356(7) Å, b = 13.0350(7) Å, and c = 9.1677(2) Å. We determine several structures using density functional theory calculations, with the lowest energy structure being Pcc2 in agreement with our experimental result. Yeelimite undergoes a reversible phase transition to a higher-symmetry phase which has been characterized to occur at 470 °C by thermodiffractometry. The higher-symmetry phase is likely cubic or pseudocubic possessing an incommensurate superstructure, as suggested by our theoretical calculations which show a phase transition from an orthorhombic to a tetragonal structure. Our theoretical study also predicts a pressure-induced phase transition to a cubic structure of space group I43m. Finally, we show that our reported crystal structure of yeelimite enables better mineralogical phase analysis of commercial calcium sulfoaluminate cements, as shown by RF values for this phase, 6.9% and 4.8% for the previously published orthorhombic structure and for the one reported in this study, respectively.