Synchrotron characterization techniques [1] are being used to study Portland-based cements and recently also CSA and related cements. A key property of these techniques is that they do not require sample preparation, so ...

The manufacturing of ye'elimite-rich cements releases from 15 to 37%, depending on their composition, less CO2 to the atmosphere than ordinary Portland cement (OPC). BYF cements containing belite, ye’elimite and ferrite ...

The manufacture of CSA cements is more environmentally friendly than that of OPC as it releases less CO2. This reduction depends on CSA composition and is due to three factors: i) less emissions from decarbonation in the ...

Cement matrices contain large amounts of crystalline phases jointly with amorphous and/or nanocrystalline phases. Consequently, their analyses are very challenging. Synchrotron powder diffraction in combination with the ...

There are many commercially important multiphase materials which contain amorphous phases, such as cement pastes, porcelains, glass-ceramics or pharmaceutical compounds. However, the analysis of amorphous phase(s) within ...

One alternative to decrease CO2 emissions from ordinary Portland Cement (OPC) production consists on the development of a new kind of eco-cements composed by less calcite demanding phases. That is the case of ...

The durability of cement-based construction materials depends on the environmental conditions during their service life. A further factor is the microstructure of the cement bulk, established by formation of cement hydrates. ...

Eco-cements are a desirable alternative to ordinary Portland cements because of their lower CO2 footprints. Some ye’elimite-based ecocements are attracting a lot of interest. Understanding the reasons for the mechanical ...

In this work, four BACSA clinkers with different compositions (belite ~ 70-55 wt %, alite ~ 10-15 wt % and ye’elimite ~ 10-15 wt %) were synthesized (at laboratory scale). Lime, gypsum, kaolin and sand were used as raw ...

Some belite-ye´elimite-ferrite (BYF) cements present low mechanical strengths mainly due to the slow reactivity of belite. A solution to this problem may be the activation of BYF clinkers by preparing them with a coexistence ...