JavaScript is disabled for your browser. Some features of this site may not work without it.

    Listar

    Todo RIUMAComunidades & ColeccionesPor fecha de publicaciónAutoresTítulosMateriasTipo de publicaciónCentrosDepartamentos/InstitutosEditoresEsta colecciónPor fecha de publicaciónAutoresTítulosMateriasTipo de publicaciónCentrosDepartamentos/InstitutosEditores

    Mi cuenta

    AccederRegistro

    Estadísticas

    Ver Estadísticas de uso

    DE INTERÉS

    Datos de investigaciónReglamento de ciencia abierta de la UMAPolítica de RIUMAPolitica de datos de investigación en RIUMAOpen Policy Finder (antes Sherpa-Romeo)Dulcinea
    Preguntas frecuentesManual de usoContacto/Sugerencias
    Ver ítem 
    •   RIUMA Principal
    • Investigación
    • Ponencias, Comunicaciones a congresos y Pósteres
    • Ver ítem
    •   RIUMA Principal
    • Investigación
    • Ponencias, Comunicaciones a congresos y Pósteres
    • Ver ítem

    Stability of epitaxial heterostructured materials

    • Autor
      Dos-Santos-Gómez, Lucía; Sanna, Simone; Esposito, Vincenzo; Pryds, Nini; Marrero-López, DavidAutoridad Universidad de Málaga; Losilla, Enrique R.
    • Fecha
      2019
    • Palabras clave
      Química; Congresos y conferencias; Heteroestructuras
    • Resumen
      Heterostructured materials are a new family of artificial compounds where the electronic and ionic properties can be modulated by varying the characteristics of the different material layers. These properties arise from the formation of structural oxygen defects in the crystal lattice that result in the activation of charge electrical carriers. Oxygen-deficient perovskite oxides, such as La1-xSrxCoO3-δ (LSC), present mixed oxide/electronic conduction; however, the long-term instability due to superficial carbonation of LSC-based cathodes is a crucial drawback for their practical application. In this study, thin film-heterostructures of alternating layers of La0.6Sr0.4CoO3-δ and Ce0.8Gd0.2O2-δ (CGO) were deposited on (110) NdGaO3 (NGO) single crystal substrates by pulsed laser deposition (PLD). The number of interfaces and the thickness were varied to obtain epitaxial structures with highly coherence layers. Moreover, two different kinds of architectures, without and with a CGO termination layer, were prepared in order to study the stability of the samples under different thermal cycles in air. Structural characterization was made by using Rocking Curve and Reciprocal Space Mapping techniques. CGO layers are rotated 45º respect to the substrate and LSC ones due to the different sizes of cell parameters. The quality of the samples was examined by HR-TEM and all of them presented well defined interfaces (Figure 1). Electrical characterization confirms that the conductivity can be modulated by varying the number of interfaces and thickness. Samples without CGO termination are unstable in air atmosphere due to surface carbonation, which was confirmed by XPS and HR-TEM.
    • URI
      https://hdl.handle.net/10630/17772
    • Compartir
      RefworksMendeley
    Mostrar el registro completo del ítem
    Ficheros
    Simposio_LdSG_Póster.pdf (105.9Kb)
    Colecciones
    • Ponencias, Comunicaciones a congresos y Pósteres

    Estadísticas

    Buscar en Dimension
    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
     

     

    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA