Belite hydration at high temperature and pressure by in situ synchrotron powder diffraction
(2020-10-16)Portland cements are currently used as Oil‐Well‐Cements for the sheath between the metal casing and the borehole. At high pressures and temperatures, the resulting C-S-H gel(s) is partly unstable and it can react to give ... -
C-S-H seeding activation of Portland and Belite cements: An enlightening in situ synchrotron powder diffraction study
(Elsevier, 2022-11)C-S-H seeding in Portland cements is well known from basic scientific works and field applications. Moreover, this activation approach could be beneficial for low-CO2 cements under development where a general drawback is ... -
A comparative study of experimental configurations in synchrotron pair distribution function
(MDPI - Publisher of Open Access Journals, 2019-04-25)The identification and quantification of amorphous components and nanocrystalline phases with very small crystal sizes, smaller than ~3 nm, within samples containing crystalline phases is very challenging. However, this ... -
Early hydration of belite-ye’elimite-ferrite cements: Role of admixtures
(sciencedirect, 2023)The effect of TIPA and CaCl2 on early hydration, i.e. 24 h, of a B-BYF cement has been studied by in situ synchrotron X-ray powder diffraction, calorimetry, thermal analysis, NMR, and rheological measurements of the pastes ... -
Local structure and Ca/Si ratio in C-S-H gels from hydration of blends of tricalcium silicate and silica fume
(Elsevier, 2021-03)At the microscale, C-S-H gels from alite, or neat Portland cements, has a Ca/Si ratio close to 1.80. At the nanoscale, C-S-H is described by a defective tobermorite structure which allows a maximum Ca/Si ratio close to ... -
Phase-selective degree of hydration at setting: An in situ synchrotron diffraction study
(Elsevier, 2022-03)Setting of Portland cements is still not well understood. Previous studies used techniques that analyse the pastes as a whole to correlate setting times with degree of hydration. Here, in-situ synchrotron X-ray diffraction ... -
Rietveld quantitative phase analyses of SRM 2686a: a standard Portland clinker
(2018-10-03)SRM 2686a is a NIST reference Portland clinker with reported mineralogical analysis from powder diffraction and electron microscopy. This sample is used in ASTM C1365 test method for Rietveld quantitative phase analysis ... -
Rietveld quantitative phase analysis with molybdenum radiation
(Cambridge Core, 2014)Building materials are very complex samples of worldwide importance; hence quantitative knowledge of their mineralogical composition is necessary to predict performances. Rietveld quantitative phase analysis (RQPA) allows ...