JavaScript is disabled for your browser. Some features of this site may not work without it.

    Listar

    Todo RIUMAComunidades & ColeccionesPor fecha de publicaciónAutoresTítulosMateriasTipo de publicaciónCentrosDepartamentos/InstitutosEditoresEsta colecciónPor fecha de publicaciónAutoresTítulosMateriasTipo de publicaciónCentrosDepartamentos/InstitutosEditores

    Mi cuenta

    AccederRegistro

    Estadísticas

    Ver Estadísticas de uso

    DE INTERÉS

    Datos de investigaciónReglamento de ciencia abierta de la UMAPolítica de RIUMAPolitica de datos de investigación en RIUMAOpen Policy Finder (antes Sherpa-Romeo)Dulcinea
    Preguntas frecuentesManual de usoContacto/Sugerencias
    Ver ítem 
    •   RIUMA Principal
    • Investigación
    • Artículos
    • Ver ítem
    •   RIUMA Principal
    • Investigación
    • Artículos
    • Ver ítem

    Activated carbon monoliths from lignocellulosic biomass waste for electrochemical applications.

    • Autor
      Ibeh, Paul O.; García-Mateos, Francisco JoséAutoridad Universidad de Málaga; Rosas-Martínez, Juana MaríaAutoridad Universidad de Málaga; Rodríguez-Mirasol, JoséAutoridad Universidad de Málaga; Cordero-Alcántara, TomásAutoridad Universidad de Málaga
    • Fecha
      2019-03-05
    • Editorial/Editor
      Elsevier
    • Palabras clave
      Lignina; Biomasa vegetal - Residuos; Acido fosfórico; Carbón activado
    • Resumen
      The valorization of lignocellulosic biomass waste into bio-based materials is proposed in this work in order to obtain low-cost materials and to reduce environmental impacts. Cylindrical activated carbon monoliths (ACMs) were prepared from Alcell®, Kraft lignin and olive stone by chemical activation with H3PO4. To our best knowledge, there is no previous information about the preparation of ACMs from any type of lignin. In this sense, the development of value-added lignin-based products could be crucial to the economic success of the bio-ethanol production within a biorefinery context. The extrusion of the adequate mixing, without any kind of binder, was carried out in an extruder designed by ourselves with different dies. Carbon monoliths without and with holes (25 or 120 channels/cm2) were obtained. In case of lignin precursors, a stabilization step was optimized to minimize the problems of plasticity and swelling of lignin. N2 adsorption–desorption at −196 °C and Hg porosimetry results show that activated carbon monoliths presented pore size distributions in the micro and mesopore range, with high surfaces areas (c.a. 1500 m2/g) and relatively high mesopore volume (0.35 cm3/g). The bulk density of the monoliths is also very high (∼1.1 g/cm3 for ACM from Alcell lignin), with compressive strength of 7.6 MPa. Electrochemical characterization of binderless activated carbon monolith electrodes was carried out by cyclic voltammetry and galvanostatic charge–discharge techniques. The ACM from olive stones presents the highest specific capacitance, with approximately 217 F/g and 205 F/cm3.
    • URI
      https://hdl.handle.net/10630/34204
    • DOI
      https://dx.doi.org/10.1016/j.jtice.2019.02.019
    • Compartir
      RefworksMendeley
    Mostrar el registro completo del ítem
    Ficheros
    2019_Paul_JTICE.pdf (6.931Mb)
    Colecciones
    • Artículos

    Estadísticas

    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
     

     

    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA
    REPOSITORIO INSTITUCIONAL UNIVERSIDAD DE MÁLAGA